The experimental results show that the addition of ZnO to the Cr 3+ doped K 2O-Al 2O 3-B 2O 3-SiO 2 glass makes the crystallizability of glass improve obviously, the crystalline temperature decrease and the nanometre grade mullite micro-crystal more uniform and regular.

研究结果表明：在K2OAl2O3B2O3SiO2系掺Cr3+玻璃的基础上引入ZnO后，析晶性能明显改善；析晶温度降低，析出的纳米莫来石微晶均匀、规则；

The results show that the influences of the glass beads content and its diameter on the tensile yield stress and strain at yield are not significant.

结果显示，微珠含量及其直径对复合物的拉伸屈服应力和屈服发生时的应变影响不太明显。

The phase of SnO__2 on F-doped SnO_2 conducting glass was characterized by X-Ray diffraction technique ( XRD), and the results show that the phases of SnO_2 belong to the tetragonal system and its average diameter is 32.35 nm.

运用XRD分析氟掺杂二氧化锡导电玻璃导电面SnO2的晶型，发现其属于四方晶系，晶粒尺寸为32.35nm。

The data of DSC and TG show that the copolymers possess excellent thermal performance, glass transition temperature over 300 ℃, thermal weight loss temperature higher than 500 ℃ and superior solubility in conventional organic aprotic polar solvents.

玻璃化转变温度高于300℃，热失重温度高于500℃。同时，聚合物在常用非质子有机极性溶剂中具有优良的溶解性能。

Experiments show that Fe 2 O 3 of low silicon iron tailings can't effectively crystallize the whole glass.

实验表明,以低硅铁尾矿中的Fe2O3作为晶核剂不能有效使玻璃整体晶化.

The results show that the pressure stress of ITO layer is the major factor that influences the warp of ITO conductive coating thin glass, the warp of ITO conductive coating glass can be reduced obviously at appropriate distribution of coating temperature.

结果表明，薄基片ITO玻璃的翘曲度主要是在镀膜时ITO膜层压应力大引起的，选择合适的成膜温度分布可明显减小ITO玻璃的翘曲度。

They saw many old things on show in glass-topped tables.

他们观看了玻璃桌面的桌子里展览的许多古老的东西.

Two people blend be close friends, show carry the cautious pattern when glass.

两人配合得要好, 表现出抬玻璃时小心翼翼的样子.

The results show that the glass Bi ( disc) and the glass eye beads of the Warring States Period all belong to the PbO-BaO-SiO2 system. According to the composition and shape, we infer that these glass Bi and eye beads were made in China.

结果表明：战国时期的玻璃璧和蜻蜓眼玻璃珠均属于PbO-BaO-SiO2玻璃，从成分和外型特征看，这些样品都为中国自制；

The results show that the value of recieved radiative heat flux between Low E glass and clear glass differs a lot under same condition.

结果表明：在相同条件下，Low E玻璃与普通透明玻璃所受到的辐射热流通量相差很大。